dvr Sodium Silicate Water Glass

Sodium silicate, also called water glass or Soluble Glass, is any one of several compounds containing sodium oxide, Na2O, and silica, Si2O, or a mixture of sodium silicates varying ratios of SiO2 to Na2O, solids contents, and viscosity. Traditionally, sodium silicates are classified according to the acid from which they are derived as Orthosilicate Na4SiO4; Metasilicate Na2SiO3; Disilicate Na2Si2O5; Tetrasilicate Na2Si4O9. They are also classified by an X-ray diffraction method according to their crystalline structure. All these compounds are colorless, transparent, glasslike substance available commercially as a powder or as a transparent, viscous solution in water. They can be dissolved in water to form a syrupy liquid. Some forms are slightly soluble, and some are almost insoluble; they are best dissolved by heating with water under pressure. The solutions are strongly alkaline. They are produced chiefly by fusing sand and sodium carbonate in various proportions. The use of sodium silicates is as a raw material for making silica gel. Also used in detergent; as a cement for glass, pottery, and stoneware; for fireproofing paper, wood, cement, and other substances; for fixing pigments in paintings and cloth printing.

 

Our Specialty:
We supply both Neutral & Alkaline sodium silicate absolute transparent quality i.e. water white.

Technical Specifications:

TESTING PROCEDURE :::
ANLYSIS PROCEDEURE OF SODIUM SILICATE : Take 5gm of sodium dilute it to 250ml in SMF with dist. Water , take 50 ml of the diluted solution add 2-4 drops of  methyl red indicator.  Then titrate it against IN {approx.}  HCL  Light Pink is the end point. Take this reading as %u201CA%u201D ml. To this solution add 5 gm of sodium fluoride dissolve properly add  6-7 drops of methyl red indicator titrate against IN HCL  appearance of slight pink colour is the end point . Take this reading as %u201CB%u201D ml 

 

CALCULATION For Na2O
 

%u201CA%u201Dml  x 3.1 x normality of HCl   = C%

               Wt. Of sample 


For  Sio2
 

%u201CB%u201Dml  x 15.02 x normality of HCl 

           Wt. Of sample X 10 

 

Ratio of sodium silicate 

 

% of SiO         i.e               D%

% of Na2o                          C%

 

Viscosity-  AS PER IS 3944 B4 CUP 

 

DETERMINATION OF IRON (as per Fe)

  • Botanic Potassium Thiocynate ;- dissolve 1.0gm of potassium thiocynate in10ml of water. Add sufficient n-butano to makeup to 100ml. Shake vigorously until the solution is clear.
  • Dilute H2SO4 :- approx.10% 
  • Standard Iron solution : weight 0.702gm of Ferrus Ammonium sulfate. Dissolve in 10ml dilute H2SO4 then make up 1000ml with water. Transfer 10 ml of this solution in 100ml M.Flask and make up 100ml with water. 1ml of this solution is equivalent to 0.01mg of iron 

 

PRCEDURE :

  • Sample Reading: take about 5gm of the sample accurately weighted. Dissolve it in distilled water and make the solution exactly 100ml. Take 10 ml of this solution add 1ml concentrated Nitric acid. Boil the solution and cool. Then transfer it into a nessler cylinder and add 30mg of Ammonium Persulfate and 15 ml of Botanic Potassium Thiocynate solution. Shake for 30 sec and allow the liquid to separate.
  • Blank reading : take 10 ml distilled water. Add 1ml concentrated Nitric acid boil the solution and cool. Then transfer it into a nesseler cylinder and add 30 mg of Ammonium Persulfate and 15 ml of Botanic Potassium Thiocynate solution . Shake for 30 sec. And allow the liquid to separate. Then add Standard Iron Solution until the colour of Butanol Layers in Both Cylinder (Sample & Blank) 
    CALCULATION :

Iron as Fe (%w)  =  0.001 V

                                     W

Where, 

V= Volume in ml of Standard Iron Solution to add in Blank Reading

W= Weight in gm of sample 

 

 

 

 

Application:

Silica gel production
Builder or anti-soil-redeposition agent for detergent
Peroxide stabilizer in bleaching for textile and pulp
Solubilizer in ink, flux binder for welding rods
Deflocculant for ceramic
Buffer
Fireproofing paper catalysts
Water treatment
Concrete hardner and acid-proof
Petroleum processing by emulsion breaking and corrosion prevention
Timber treatment.
Oil Field use
 

Range of Products:
Sodium Silicate liquid both Neutral & Alkaline
We manufacture large range of Sodium Silicate both in Neutral and Alkaline grade of the typical qualities.

We also manufacture Sodium Silicate as per the customer's requirements and specification.

Sodium Silicates Concentration Mole Ratio Baume
Alkaline Sil 40 – 54 % 2.1 to 2.6 45 – 57
Neutral Sil 27 – 39 % 3.0 to 3.5 30 – 41.5
Using Procedure:

 

Sodium Silicate is a compound mixture of sodium oxide i.e. Na2o with silica sand i.e. Sio2 with water. Sodium silicate is also called water glass. There are two process to manufacture liquid Sodium Silicate. 

To manufacture a lower ratio of Sodium Silicate by Hydrothermal process.

Mixture at Na2Co3 (Soda Ash) with Sio2(Silica sand) in furnace fuses  of more then 1100oC gives sodium silicate glass in lumps form which is  easily dissolved in hot water.We manufacture large range of sodium silicates, as per the customer's specific requirements.
 

Note:

PRODUCT IDENTIFICATION
CAS NO.  ……. .1344-09-8 
EINECS NO… .215-687-4
FORMULA …… 2Na2O.SiO2
MOL WT.  ……..184.04
H.S.CODE……. 2839.19

 

SODIUM METASILICATE (5H2O)

Sodium Metasilicate 5H2o is used in Tanning Industries, Leather Industries, Metal Treatment, Washing Powder etc. available in Powder form of various mess size.

SILICA GEL
It is available in white and blue colour Indicating & Non-Indicating type with Sio2 content 97-98 %. It observes the moisture. It is used in electrical goods, telephone system, All electronic items, In Pharmaceuticals, In chemical Process. Available in sachet of 1 to 25 gms and also in bulk packages of 25 kgs or 50 kgs in Fibre drum.

 

 

Our proximity to the International port helps us to give fast reliable and efficient delivery to our overseas customers. We have exported to various countries like Netherlands , Iraq , Malaysia ,Saudi Arabia and UAE to name a few.

 

Note: This article uses material from the http://rxmarine.com/